在超声波作用下采用一步合成法分别制备三乙基硼、三丙基硼和三丁基硼;考察超声波作用对合成产物产率的影响,用红外光谱及元素分析表征合成产物的结构;以合成的三乙基硼、三丙基硼和三丁基硼为原料通过热裂解制备纯度较高的碳化硼超硬材料;讨论不同原料和裂解温度对合成产物中C含量的影响。研究结果表明:以三乙基硼为原料在温度为1 400 K进行裂解时,其裂解产物中B4C, B2O3和裂解自由碳的含量分别为94.0%...
Absorption rate of CO2 into aqueous solution of N-methyldiethanolamine (MDEA) blended with di-ethanolamine (DEA) and piperazine (PZ) was studied and a kinetic model was established. It is shown that...
High-pressure phase behavior of supercritical (SC) CO2+ethanol system was investigated at 333.2 K, 348.2 K, 353.2 K, 368.2 K, 413.2 K and 453.2 K and pressure from 2.0 MPa to 14.3 MPa. The measureme...
氯化2,3,5-三苯基-2氢-四唑及2,4,6-三(2-吡啶基)-s-三嗪在HCl中对碳钢的缓蚀作用
corrosion inhibition quantum chemistry electrochemical measurement
2009/3/5
Electrochemical measurement, quantum chemical method, and scanning electron microscopy (SEM) were performed to investigate the inhibitive effect of 2,3,5-triphenyl-2H-tetrazolium chloride (TTC) and 2,...
TiC powder was synthesized by mechanical alloying of titanium and asphalt in this paper. Deoiled asphalt as a carbon source not only provided element C in the fabrication of TiC but also cracked itsel...
新一代碳吸附剂的环保生产
环保生产 碳吸附剂
2008/12/17
现已成功研究出能满足新一代吸附材料要求的新型火性碳生产工艺和设备。该现代化设备生产效率高,有很强的盈利能力。该工艺技术处理过程独特,采用中度和高度变质的矿物原料,所用设备能保证纯净度在99.8%以上,这使得其产品质量和几个指标均优于国内和国外同类产品,在世界市场上有很强的竞争力。此钟新型吸附剂机械强度提高到92%(同类产品为82-85%),碘的吸附额达1150-1300毫克/升(同类产品为950-...
用煤矸石制备β-赛隆结合碳化硅复相粉体的方法
煤矸石 碳化硅b-赛隆
2008/12/3
用煤矸石制备β-赛隆结合碳化硅复相粉体的方法属材料技术领域。该发明选用煤矸石为原料,其中SiO_2质量百分比为60%~70%,Al_2O_3质量百分比为10%~20%,碳含量5%~10%,用盐酸酸洗除铁,水洗至pH为中性。将煤矸石细粉与碳粉按100∶15~45的比例混合,加水湿磨,烘干。在氮气气氛下1400~1600℃烧结,保温后冷却,然后在600~800℃煅烧除去残余的碳,即得β-Sialon结...
吸热型碳氢燃料热裂解焦的性质研究
结焦 氢碳比 渗碳 吸热型碳氢燃料
2008/6/16
采用挂片测焦的方法,测定了吸热型碳氢燃料S-1结焦速率随裂解时间的变化,结果显示随反应时间的延长,燃料的结焦速率基本呈现增加趋势。利用能量弥散X射线分析对金属挂片渗碳现象的考察结果显示,挂片焦中明显有金属原子的迁移。还利用仪器分析手段对吸热型碳氢燃料S-1在700 ℃时裂解所生成焦的性质进行了考察,元素分析结果显示随反应时间的延长焦的氢碳比变低,扫描电镜对焦表面形态结构的研究结果显示热处理温度对焦...